China Plastic Raw Material Virgin High Density Polyethylene HDPE Granules for Transparent Bags

Product Description

Product Description

Product Number:
HDPE PN049,HDPE-100,HDPE-80,HDPE-6081H,HDPE-3000JE,HDPE-32F,HDPE-B507,HDPE-B502,HDPE-XP9020,
HDPE-6098, HDPE-TR400N,HDPE-YEC-5505T,HDPE-5000S,HDPE-1158,HD6007XA,etc.

Description:

HDPE is a highly crystalline non-polar thermoplastic resin produced through the copolymerization of ethylene and a small amount
of α-olefin monomer. HDPE is synthesized under low pressure and is therefore also called low-pressure polyethylene. HDPE is
mainly a linear molecular structure and has little branching. It has a high degree of crystallization and high density. It can withstand
high temperatures and has good rigidity and mechanical strength and anti-chemical corrosion.we produces a full grade of HDPE,
which cover all fields of HDPE applications, including film, blow-molding, extrusion molding, injection molding, pipes, wire & cable
and base material for producing chlorinated polyethylene.

Product Parameters

Grades	HDPE PN049	HDPE-100	HDPE-80	HDPE-6081H	HDPE-3000JE
(5.0kg,190ºC)Melt mass-flow rate ,g/10min	0.26	0.26	0.43	6.22	2.2
Density,g/cm³	0.95	0.95	0.9458	0.9577	0.956
Tensile stress at yield,Mpa	23.3	23.3	21.3	26.1	24.8
Modulus of elasticity in tension,Mpa	882	882	-	-	-
Flexural modulus,Mpa	1047	1047	955	1057	1020
23ºC Charpy impact strength,KJ/m²	37.8	37.8	11.8H	4.2	12
Temperature of deflection under load(Tf0.45),ºC	77	77	-	-	68
Water content,mg/kg	14	14	58	-	-
Volatile content,mg/kg	213	213	112	-	-
0xidation induction time(0IT,210ºC),min	78.3	78.3	28.9	-	-
Nominal tensile strain at break,%	560	560	298	661	9.6
Application	drain pipe	drain pipe	Water pipe	Injection bottle cap	Injection bottle cap

 

Grades	HDPE-32F	HDPE-B507	HDPE-B502	HDPE-XP9020	HDPE-6098
(5.0kg,190ºC)Melt mass-flow rate,g/10min	1.98	6.43	1.86	0.14	0.38
Density,g/cm³	0.9373	0.948	0.9507	0.941	0.9494
Tensile stress at yield,Mpa	16.8	21.7	23.6	220	22.5
Modulus of elasticity in tension,Mpa	-	-	969	-	-
Flexural modulus,Mpa	741	-	-	6200	-
23ºC Charpy impact strength,KJ/m²	28.6P	-	43.1P	-	-
Temperature of deflection under load(Tf0.45),ºC	127.2	-	-	-	-
Water content,mg/kg	22	-	-	-	-
0xidation induction time(0IT,210ºC),min	65.7	-	-	-	-
Nominal tensile strain at break,%	869	850	774	>600	466
Application	PEX-A floor heating pipe	various types of bottles, cans and industrial tanks and barrels	various types of bottles, cans and industrial tanks and barrels	Floor heating pipe	Shopping bag,market bag,garbage bag,drain pipe,etc.

 

Grades	HDPE-TR400N	HDPE-YEC-5505T	HDPE-5000S	HDPE-1158	HD6007XA	HDPE-QHJ01
(5.0kg,190ºC)Melt mass-flow rate,g/10min	11.6(21.6kg)	0.7	1	2.1	0.6	0.7
Density,g/cm³	0.939	0.945	0.951	0.953	0.962	0.945
Tensile stress at yield,Mpa	20	19	25	24	30.5	18
Flexural modulus,Mpa	-	-	-	-	1700	9
23ºC Charpy impact strength,KJ/m²	-	-	-	32	-	-
Nominal tensile strain at break,%	799	500	800	600	300	500
Application	Blow molding geomembrane products	Base Resin of Chlorinated PolyethyleneBase Resin of Chlorinated Polyethylene	Package film, nets, ropes and small and medium-sized containers	Blow Molding Grade	Blow Molding Grade	Cable and wire