Prime Grade Virgin Plastic Particle LDPE Low-Density Polyethylene Resin Granules
|
Still deciding? Get samples of $ !
Request Sample
|
| Customization: | Available |
|---|---|
| Feature: | Nograde |
| CAS No.: | 9002-88-4 |
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Test Report
Find Similar Products
Basic Info.
- Model NO.
- LDPE Granules
- Formula
- (C2h4)N
- EINECS
- 618-339-3
- Material
- Low Density Polyethylene/LDPE
- Usage
- General Plastics, Engineering Plastics, Specialty Plastics
- Plastic Properties After Heated
- Thermoplastic Plastics
- Plastic Forming Method
- Film/Injection Mold/ Blow Mold/Pipe Cable Grade
- Color
- White
- Features
- High Fluidity and Good Processability
- MOQ
- 1tonm
- Density
- 0.918~0.935g/cm3
- Keywords
- LDPE Film Grade Granules
- Transport Package
- 25kg/Bag
- Specification
- 25kg/bag
- Trademark
- HEBEI CHANGSHENG
- Origin
- China
- HS Code
- 3901100090
- Production Capacity
- 2000mt/Month
Product Description
Low-density polyethylene(LDPE)is a synthetic resin using a high pressure process via free radical polymerization
of ethylene and is therefore also called "high-pressure polyethylene". Since its molecular chain has many long
and short branches, LDPE is less crystalline than high-density polyethylene (HDPE) and its density is lower. It
features light, flexible, good freezing resistance and impact resistance. LDPE is chemically stable. It has good
resistance to acids (except strongly oxidizing acids), alkali, salt, excellent electrical insulation properties. Its
vapor penetration rate is low.LDPE has high fluidity and good processability. It is suitable for being used in
all types of thermoplastic processing processes,such as injection molding, extrusion molding, blow molding,
rotomolding, coating, foaming, thermoforming, hot-jet welding and thermal welding.
| Grades | LD165 | LDPE-2100TN00 | LDPE-18G | LDPE-1C7A | LDPE-2426F | LDPE-2426H | LDPE-2420D |
| Density,g/cm³ | 0.9214 | 0.9192 | 0.918 | 0.918 | 0.923 | 0.923 | 0.9225 |
| MFR,g/10min | 0.30 | 0.308 | 7 | 7 | 0.8 | 1.9 | 0.25 |
| Stretching broken column nominal strain,% | 548 | 529 | - | - | MD200 TD600 |
600 | - |
| Tensile strength at broken,
Mpa
|
15.8 | 14.5 | - | - | MD26 TD20 |
15 | 10 |
| Haze,% | 10 | - | - | - | - | 8 | <14 |
| Fisheye(0.3mm-0.2mm),
qty/1200cm²
|
25 | - | - | - | - | - | - |
| Swell ratio,/ | - | - | 1.55 | 1.7 | - | - | - |
| Turbidity,% | - | - | - | - | <8 | - | - |
| Gloss,% | - | - | - | - | >40 | - | (20ºC)>15 |
| Film Thickness,μm | - | - | - | - | 50 | - | (60ºC)50 |
| Modulus of Elasticity,Mpa | - | - | - | - | 260 | - | 240 |
| Dart Impact Strength,g | - | - | - | - | 130 | - | - |
| Vicat Softening Point,ºC | - | - | - | - | 94 | - | 94 |
| DSC Melting Point,ºC | - | - | - | - | 11 | - | 109 |
| Application | Tubular film | Tubular film | Film | cardboard, packaging | Film | Film | Film,blow-molded hollow products |
| Grades | LDPE-1C7A | LD605 | LD100BW | LDPE1l50A |
| Density,g/cm³ | 0.918 | 0.922 | 0.923 | 0.923 |
| MFR,g/10min | 7 | 6 | 2.1 | 50 |
| Stretching broken column nominal strain,% | - | 100 | - | - |
| Tensile strength at broken,Mpa | - | 8 | 11 | 6 |
| Haze,% | - | - | - | - |
| Fisheye(0.3mm-0.2mm), qty/1200cm² |
- | - | - | - |
| Swell ratio,/ | 1.7 | - | - | - |
| Turbidity,% | - | - | - | - |
| Gloss,% | - | - | - | - |
| Film Thickness,μm | - | - | - | - |
| Modulus of Elasticity,Mpa | - | - | - | - |
| Dart Impact Strength,g | - | - | - | - |
| Vicat Softening Point,g | - | - | - | - |
| DSC Melting Point,ºC | - | - | - | - |
| Application | cardboard, packaging | civil detonators, pipes, plates and injection-molding products | Wire&Cable Grade | Artificial Flower Grade |
){kind=link}
Send your message to this supplier
People who viewed this also viewed
Product Groups
Find Similar Products By Category
- Supplier Homepage
- Products
- PP/HDPE/LDPE/LLDPE
- LDPE Granules
- Prime Grade Virgin Plastic Particle LDPE Low-Density Polyethylene Resin Granules